Covet International recently commissioned an independent ASTM B117 salt fog test to evaluate Ever Art Wood's resistance to atmospheric corrosion. This was in addition to various accelerated ageing tests conducted on Covet’s popular timber look aluminium cladding range.

Read about the test, the process and how well Ever Art Wood performed after 500 hours of exposure.

Some of the most breathtaking settings for beautiful buildings are also some of the harshest environmental conditions. When coastal buildings are lashed by wind, fog, salt, rain, and, of course, the harsh Australian sun, it’s important to build them using a material palette that will endure and last for a long time.

Designers and architects need to be confident that their chosen building materials will perform over many years of service when exposed to the elements day in, day out.

When a timber aesthetic is desired in such environments, timber look aluminium products provide designers an infinitely more viable option than genuine timber. Timber look aluminium, however, is still subject to the threat of atmospheric corrosion, which could degrade the surface of the material through prolonged exposure to water and water soluble pollutants such as salt. Corrosion can impact not only the base metal of timber look products but the timber look finish too. Both the base metal and coating need to be durable enough to endure the ongoing impacts of salt, moisture and humidity.

Manufactured in Japan, the Ever Art Wood range is comprised of pre-finished aluminium extrusions and sheets, with a machine applied timber look wrap. Covet set out to prove just how durable Ever Art Wood cladding is, subjecting it to a rigorous independent ASTM B117 salt fog test for corrosion resistance.

About salt fog testing

Corrosion testing determines how metal components and parts perform when exposed to environmental conditions that may cause them to corrode. Using a controlled environment, the rate of corrosion can be accelerated with salt exposure to compare materials or material combinations.

Internationally recognised and one of the most widespread and long-established corrosion tests, the salt fog or salt spray test is conducted all over the world in various industries including automotive, aerospace and military applications. One of a suite of accelerated ageing tests, it subjects metals and coated metal products to corrosive attack in order to evaluate the suitability of the material for use in corrosive environments.

The purpose of the test is to evaluate the corrosion resistance and durability of both the base metal and coatings applied. The effect of corrosion is evaluated through observation of the test specimen’s appearance following a specified period within the test chamber – specifically looking for blistering, loss of adhesion of the coating, corrosion of the base metal, or any other abnormalities including the presence of rust or other oxides.

About the Standard ASTM B117 and the testing process

ASTM B117 was the first internationally recognised salt spray standard. Originally published in 1939, it outlines the standard practice for operating Salt Spray (Fog) Apparatus.

Salt fog chamber

Salt fog chamber

The salt fog test involves placing a test specimen in a salt fog chamber. A salt solution set at neutral pH is fed into the chamber via an atomiser. Conditions in the chamber are set at condensing humidity – with the test samples constantly ‘rained on’ or sprayed with salt solution at a temperature of 35 degrees Celsius. The resulting environment of dense saltwater fog produced in the chamber exposes the test specimens to severely corrosive conditions.

The test duration varies depending on the specimens being tested and their expected corrosion resistance. For example, a typical test duration for pre-treated and painted metal components is 96 hours.

Testing Covet Ever Art Wood

Covet Ever Art Wood was tested by the Product Testing Division of the Australian Wool Testing Authority, a certified NATA Lab in Melbourne.

Test Machine: Salt Spray (Fog) Apparatus
Testing duration: 500 hours
Testing Process:
- Six samples of Ever Art Wood were tested, including three different profiles - a batten extrusion closed with end caps, an open batten extrusion and a flat panel sheet.
- Testing process as Standard Practice for Operating Salt Spray (Fog) Apparatus ASTM B117-2018
Test Parameters: Salt solution set at neutral pH. Salt solution is fed into the chamber via an atomiser. Samples subjected to constantly condensing levels of humidity at temperature of 35 degrees Celsius.

The Results

Two material tests from Covet’s Ever Art Wood palette were conducted – Kuri Masame (light) and Burakku Eboni (dark).

Sample A: Kuri Masame End Cap Open

Sample A: Kuri Masame End Cap Open

Appearance Assessment

Blistering: Nil
Base Metal Corrosion: Nil
Loss of Adhesion: Nil
Other abnormalities: Nil

Sample D: Burakku Eboni Open

Sample D: Burakku Eboni Open

Appearance Assessment

Blistering: Nil
Base Metal Corrosion: Nil
Loss of Adhesion: Nil
Other abnormalities: Nil

Sample B: Kuri Masame End Cap Closed

Sample B: Kuri Masame End Cap Closed

Appearance Assessment

Blistering: Nil
Base Metal Corrosion: Nil
Loss of Adhesion: Nil
Other abnormalities: Nil

Sample E: Burakku Eboni End Cap Closed

Sample E: Burakku Eboni End Cap Closed

Appearance Assessment

Blistering: Nil
Base Metal Corrosion: Nil
Loss of Adhesion: Nil
Other abnormalities: Nil

Sample C: Kuri Masame Sheet

Sample C: Kuri Masame Sheet

Appearance Assessment

Blistering: Nil
Base Metal Corrosion: Nil
Loss of Adhesion: Nil
Other abnormalities: Nil

Sample F: Burakku Eboni Sheet

Sample F: Burakku Eboni Sheet

Appearance Assessment

Blistering: Nil
Base Metal Corrosion: Nil
Loss of Adhesion: Nil
Other abnormalities: Nil

The verdict

After continuous exposure over a robust period of 500 hours, no change in the appearance of the product was observed in any of the six samples tested. The assessment revealed nil change overall, and absence of commonly observed corrosion characteristics including blistering, base metal corrosion, loss of adhesion or any other abnormalities.

Additionally, comparison between a control sample and the samples tested showed no visible fading of the Ever Art Wood timber look finish.

These test results, in conjunction with the performance of Ever Art Wood in other accelerated ageing tests, provide designers with confidence that Ever Art Wood can stand up to the challenges of Australia’s harshest conditions over many years.